Self-Drying Type High Transparent High Hardness Wear-Resistant Nano Resin

Product Description

We are indulged in Making, Exporting and Supplying Self-Drying Type High Transparent High Hardness Wear-Resistant Nano Resins in Shanghai, China. This product is a transparent nano resin used in the fields of high hardness, high transparency, wear resistance, hardening and protection. The hardness of this product can reach pencil hardness 7~9H. It can be bent without cracking, acid and corrosion resistance (480hrs salt water test), excellent scratch resistance, and can be widely used in the preparation of transparent glass heat-insulating resin, transparent UV-resistant resin, also It can be used for transparent and hard protective top coat on metal, plastic, tile, wood and decorative materials. It can also be used in golf equipment, bicycles, rackets and other sports equipment and leather industry. It is hardened at room temperature, and the solvent is low in toxicity and easy to decompose. a Product Featuresa a Main ingredients: silicone modified resin. a Solid content: 35% a Appearance: colorless transparent liquid. a Transparency: visible light transmittance is greater than 90% a Compatibility: compatibility and compatibility with functional nano-slurry and UV absorber. a Viscosity: 102 mpa.s a Specific gravity: 920 g / l a HP value: 8 a Main solvent: n-butanol: isopropanol = 1:1 a Adapt to the temperature: minus -30~+180 degrees C, the hot water can not directly contact with the foam. a Dip or whitening hardness: 7~9H (harder than ordinary tiles). a Corrosion resistance: 480hrs brine test (coating thickness 35micro aluminum sheet). a Zigzag: 90 degrees 4 times (coating film thickness 15micro aluminum sheet). a Antibacterial: The surface is dense and the bacteria cannot remain. a Easy to clean: foreign matter can not be sticky, anti-fingerprint (easy to clean) ability. a Resistant to pollution: soy sauce, ink, signature pen, wiped without leaving any lines. [Package Specifications] A 20kg / plastic bucket. a Instructionsa 1. Use it directly or after moderate dilution with thinner or slow-drying thinner. 2, coating method: spraying, dip coating, roller coating. 3. Drying conditions: self-drying or heating. After coating, it can be dried for 20 minutes and dried for one week. Or bake at 125 degrees Celsius for 60 minutes; or bake at 140 degrees Celsius for 45 minutes. 4, the dry film thickness of the coating film should not exceed 35micro, more than cracking when completely dry, there is a demand for the product thickness of the product should not exceed 10~15micro. a Precautionsa 1. This product can be used for 50 days at room temperature of 25 degrees Celsius. It can be kept for 90 days at 2~6 degrees Celsius. If it is found that there is a glue (GEL) phenomenon, it is not applicable. 2. This product can only be painted on the upper layer. It can not be coated with other resin according to the coating. If it needs to be removed by strong physical blasting or removing paint, strong acid (except hydrofluoric acid), strong alkali, or solvent. Can not be removed. 3. For PU or acrylic resin or baking varnish, it has good adhesion. As long as there is no oil ester or dust on the surface, it can be sprayed without grinding. 4. For magnesium aluminum/lithium alloy, it is easy to have very good adhesion characteristics and anti-corrosion effect. 5. This product is a flammable item, please keep it in a dry and cool place, and keep away from fire and children's places. 6. The operator should be in a well-ventilated place, and wear rubber gloves, protective clothing, goggles construction. 7. If the skin is contaminated, wipe it off with (ethanol) and wash it with detergent and water.